Structural Composite Lumber (SCL)



Authors as Published

Authored by Henry Quesada, Professor and Extension Specialist, Purdue University; Sailesh Adhikari, Research Associate, and Robert Smith, professor. Department of Sustainable Biomaterials, Virginia Tech.

What is SCL?

Structural composite lumber (SCL) is an engineered wood product manufactured by layering strands, veneers, or flakes with adhesive into material blocks known as billets. The term SCL was used to capture the variety of unique structural products that include parallel strand lumber (PSL), laminated strand lumber (LSL), laminated veneer lumber (LVL), and oriented strand lumber (OSL). For all SCL billets, the grain of each layer ran in the same direction. SCL has been successfully used for various construction purposes, including headers, truss chords, rafters, beams, joists, columns, I-joist flanges, and wall studs.

Photo of lumber structual frames
Figure 1: SCL on Structural application. Source (APA, 2021)

SCL is manufactured to some standard size, then resawn into specified sizes based on the product end- use. Some SCL products are available in several thicknesses, while others are only produced in standard 45 mm thickness. Typical depths of SCL members range from 241 to 606 mm. Single SCL members may be nailed or bolted together to form built-up beams. Generally, SCL is available in lengths of up to 20 m. Some of the major SCL producers from the US are listed in Table 1.

Table 1: APA certified SCL manufacturers from the US

Manufactures City State
Boise Cascade Company Boise Idaho
Roseburg Forest Products Company Roseburg Oregon
Murphy Company Eugene Oregon
Pacific Woodtech Corporation Burlington Washington
Sound Wood Products Inc Chehalis Washington
Roseburg South Engineered Wood Roseburg Oregon
Freres Lumber Co Inc. Lyons Oregon

Design Specification of SCL

SCL is a proprietary product, so each manufacturer's design value is specific. Using SCL in the structural application requires information on the design properties of each product type specific to the company. As an example, the design values of different SCL types from Weyerhaeuser are included in Table 2.

Laminated veneer lumber (LVL)

LVL is manufactured from thin veneer layers to form larger beams and columns. These layers are glued together under high pressure and heat to make solid panels. In LVL, the grain of each veneer layer runs in the same direction so that it can be loaded on its short edge as a beam or as a plank in a wide face. Generally, LVL is made from rotary-peeled veneers. A diverse range of species can be used to produce LVL, such as pine, larch, Douglas-fir, and spruce. Because of the material choice and production procedure of LVL, they are stronger, straighter, and more uniform than solid timber. LVL has primarily been used in structural framing for residential and commercial construction. Common applications of LVL in construction include hip and valley rafters, flange material for prefabricated wood I-joists headers and beams, and scaffold planking. LVL has been used in roadway signposts and as truck bed decking. First used during World War II to make airplane propellers, laminated veneer lumber (LVL) has been available as a construction product since the mid-1970s. LVL is the most widely used structural composite lumber (SCL) product because of its strong dimensional attributes and rigidity.

Photo of two laminated veneer lumbers
Figure 2: Laminated Veneer Lumber (LVL)(Chirag Enterprises, 2021; CWC, 2021a)

The LVL panels are cut into a range of widths depending on the product's end-use. The most common thickness of LVL is 45 mm but LVL thicknesses vary from 19 mm to 178 mm. Manufacturers commonly produce the LVL with standardized depths of 241 mm, 302 mm, 356 mm, 406 mm, 476 mm, and 606 mm. Wider beams are constructed by attaching multiple LVL plies. LVL is also available in lengths up to 24.4 m, while more common lengths are 14.6 m, 17 m, 18.3 m, and 20.1 m.

Laminated strand lumber (LSL)

LSL is another engineered wood product made from flaked wood strands with a length-to-thickness ratio of approximately 150. The strands are oriented and formed into a large mat or billet before applying glue with heat and pressure to convert into solid wood. The strands in LSL are set up parallel to the member's longitudinal axis, which is different from OSB. LSL also does not have a common standard of production and common design values.

LSL is predominantly used in structural framing for commercial, residential, and industrial construction. It is appropriate for millwork, tall wall studs, headers and beams, sill plates, rim boards, and window framing. LSL has good fastener-holding strength and provides design flexibility for exposed parts.

Photo of two laminated strand lumbers
Figure 3: Laminated Strand Lumber (LSL).(CWC, 2021b; Naturally Wood, 2021a)

Oriented strand lumber (OSL)

OSL is made from flaked wood strands with a length-to-thickness ratio of approximately 75. The wood strands used in OSL are shorter than those in LSL. The strands are oriented and formed into a large billet to get the solid wood product after applying glue under heat and pressing. OSL looks like an oriented strand board (OSB) in physical appearance. They are both fabricated from similar wood species and contain flaked wood strands. However, unlike OSB, the strands in OSL are arranged parallel to the member's longitudinal axis.

Photo of two oriented strand lumbers
Figure 4: Oriented strand lumber (OSL).(CWC, 2021c; Intense Research, 2021).

Parallel strand lumber (PSL)

PSL is a solid engineered wood product. It is made from flaked wood strands arranged parallel to the member's longitudinal axis and has a length-to-thickness ratio of approximately 300. Combined with an exterior waterproof phenol-formaldehyde adhesive, the strands are oriented and formed into a large billet, then pressed together and cured using microwave radiation. Natural defects such as knots, grain slope, and splits have been distributed all over the material or removed entirely during manufacturing.

Photo of two parallel strand Lumbers
Figure 5: Parallel Strand Lumber (PSL).(CWC, 2021d; Naturally Wood, 2021b)

PSL also does not have a common standard of production and common design values, so it is specific to manufacturers. PSL beams are available in 68 mm, 89 mm, 133 mm, and 178 mm thickness and a maximum depth of 457 mm. PSL columns are available in 89 mm, 133 mm, and 178 mm square or rectangular dimensions. The smaller thicknesses can be used individually as single plies or combined for multi-ply applications. PSL is usually limited to 20 m in length due to transportation constraints. PSL is the only SCL type that can be pressure treated and used outside in an exposed environment.

Why use SCL?

  • The major advantage of SCL in the US is that it is available through lumber distribution systems, so availability is not an issue as it might be with glulam.
  • SCL helps to meet the increasing demand for structural lumber products with highly reliable strength and stiffness properties. Because of material choice and production procedure, SCL products can take greater loads than the sawn timber equivalent.
  • SCL is much less prone to warping, splitting, or shrinking when compared to sawn timber, so it offers structural integrity and stability.
  • SCL offers more diversity in sizes and dimensions and provides working flexibility.
  • SCL is a highly sustainable product, as they sequester significant amounts of carbon and increase the energy efficiency of the building.
  • SCL utilizes a higher percentage of scraps from timber production. Reusing these valuable resources reduces the amount of timber harvesting required to maintain adequate production levels, which preserves more forest area.
  • With its ability to be manufactured using small, fast-growing, and underutilized trees, SCL products efficiently use forest resources and help in forest management.
  • SCL also offers efficiency in the installation process's working time and labor costs. Some SCL types offer the lowest density products at maximum strength, assisting in lowering foundation work and cost.

Limitations of using SCL

  • The cost of the SCL is a major concern to many builders. As SCL adds more labor time and processing work during its production, they are comparatively costlier than structural grade lumber though the cost per strength of SCL higher than structural lumber.
  • SCL studs are usually denser and heavier than structural grade lumber, so they're more difficult to nail.
  • Wood does not like moisture and water exposure, and especially SCL can't stand exposure to humidity. After exposure to moisture, SCL easily discolors, warps, expands, and rots faster than dimensional lumber.
  • In most cases, the manufacturing process involves the usage of urea-formaldehyde resin, and it makes the boards toxic.


The Department of Sustainable Biomaterials at Virginia Tech would like to thank the Softwood Export Council (SEC) for providing the funding for the production of this fact sheet.


APA. (2021). Structural Composite Lumber (SCL) - APA – The Engineered Wood Association.

Chirag Enterprises. (2021). Laminated Veneer Lumber LVL Board.

CWC. (2021a). Laminate Veneer Lumber - The Canadian Wood Council - CWC.

CWC. (2021b). Laminated Strand Lumber - The Canadian Wood Council - CWC.

CWC. (2021c). Oriented Strand Lumber - The Canadian Wood Council - CWC.

CWC. (2021d). Parallel Strand Lumber - The Canadian Wood Council - CWC.

Intense Research. (2021). Global and China Oriented Strand Lumber Market 2016 Size, Key Trends, Demand, Growth, Size, Review, Share, Analysis to 2021 2016-05-02.

Naturally Wood. (2021a). What is Laminated Strand Lumber (LSL)? - naturally: wood.

Naturally Wood. (2021b). What is Parallel Strand Lumber (PSL)?

Weyerhaeuser. (2021). Design information for TimberStrand LSL, Microllam LVL and Parallam PSL.

Table 2: Design values in PSI of LSL, LVL, and PSL at 100% load duration Source: (Weyerhaeuser, 2021)

SCL Product TimberStrand® LSL
SCL Grade 1.3 E 1.55E
Orientation Beam/Column Plan Beam
G (Shear Modulus of Elasticity) -Kpa 560,199 560,199 667,929
E (Modulus of Elasticity x 106) -Kpa 8 8 10
Emin (Adjusted Modulus of Elasticity) -Kpa 4,555,710 4,555,710 5,431,792
Fb (Flexural Stress) -Kpa 11,721 13,100 16,030
Ft (Tension Stress) -Kpa 8,963 8,963 8,894
Fc⊥ (Compression Perpendicular to Grain) -Kpa 4,895 4,619 6,205
Fcll (Compression Parallel to Grain) -Kpa 12,651 12,651 14,961
Fv (Horizontal Shear Parallel to Grain) -Kpa 2,930 1,034 2,137
SG (Specific Gravity) 0.5 0.5 0.5
SCL Product Microllam® LVL Parallam® PSL
SCL Grade 2.0E 1.8E 2.2E
Orientation Beam Column Beam
G (Shear Modulus of Elasticity) -Kpa 861,844 775,660 948,029
E (Modulus of Elasticity x 106) -Kpa 13 12 15
Emin (Adjusted Modulus of Elasticity) -Kpa 7,008,761 6,307,875 7,709,648
Fb (Flexural Stress) -Kpa 17,926 16,547 19,994
Ft (Tension Stress) -Kpa 1,3065 13,755 15,857
Fc⊥ (Compression Perpendicular to Grain) -Kpa 5,171 3,757 4,309
Fcll (Compression Parallel to Grain) -Kpa 1,7305 17,236 19,994
Fv (Horizontal Shear Parallel to Grain) -Kpa 1,965 1,310 1,999
SG (Specific Gravity) 0.5 0.5 0.5

Virginia Cooperative Extension materials are available for public use, reprint, or citation without further permission, provided the use includes credit to the author and to Virginia Cooperative Extension, Virginia Tech, and Virginia State University.

Virginia Cooperative Extension is a partnership of Virginia Tech, Virginia State University, the U.S. Department of Agriculture, and local governments. Its programs and employment are open to all, regardless of age, color, disability, sex (including pregnancy), gender, gender identity, gender expression, genetic information, ethnicity or national origin, political affiliation, race, religion, sexual orientation, or military status, or any other basis protected by law.

Publication Date

May 9, 2022